Leaded Brass Wires

We offer a variety of Brass Wire, Brass Flat Wire, Square Brass Wire which are extensively used in automobile, electronic, electric & nipples. Our range of brass wire mesh is acclaimed for its durability, excellent performance and minimal prices.
We also offer various other grades of Brass Wire like Riveting Brass Wire, Forging Grade Brass Wire, Free Cutting Grade, EDM Brass Wire, Lead Free Brass Wire - IS:2074, BS:2874 CZ119, IS:4170/75, CuZn38PB1, Free Cutting - BS249, IS:319 Gr. l & ll, IS:8364 Gr. l & ll, BS:2874 CZ121Pb3, CuZn39Pb3, Lead Free, IS4413, CuZn37, DTD-627, 60:40.

Riveting Brass Wire

• IS:2074
• BS:2874CZ119
• IS:4170/75
• CuZn 38PB1 / 1.5
• CZ129

Chemical Requirements	CZ119		CZ129
	CuZn37Pb2		CuZn38Pb1
Copper	61.0 - 64.0%		59.0 - 62.0%
Lead	1.0 - 2.50%		0.80 -1.50%
Iron	0.15%max		0.15%max
Total Imp.	0.30%		0.50%
Zinc	Reminder		Reminder
Physical Properties	CZ119		CZ129
Condition	T.S. MPA	EL % Min	T.S. MPA	EL % Min
Manufacturing	350-380	22	350-380	25
Fabrication Properties	CZ119		CZ129
Capacity for being
Cold worked	Fair		Fair
Hot formed	Excellent		Excellent
Machinability Rating	80%		80%
Suitability for soldering	Fair		Excellent
Suitability for Brazing	Good		Good
Application :
Typically used: Fasteners, Rivets, Domestics application, Automotive Engineering
Hose Fittings , Intricate parts such as clock components.

Chemical Requirements		Grade I		Grade II		Grade III
Copper		56.0 - 59.0%		60.0 - 63.0%		60.0 - 63.0%
Lead		2.0 to 3.50%		2.50 - 3.70%		0.50 - 1.50%
Iron		0.35% max		0.35% max		0.20% max
Total Imp. Excl. Iron		0.70% max		0.50% max		0.50% max
Zinc		Remainder		Remainder		Remainder
Physical Properties		Grade I		Grade II		Grade III
Condition	Size	T.S. MPA	EL% Min	T.S. MPA	EL% Min	T.S. MPA	EL% Min
Annealed (O)	6-25 25-50 50 above	345 315 285	12 17 22	355 305 275	15 20 25	315 285 255	22 27 32
Half-Hard (HB)	6-12 12-25 25-50 50 above	405 395 355 325	4 6 12 17	395 385 345 315	7 10 15 20	355 345 305 285	8 12 22 27
Hard (HD)	6-12 12-25	550 485	- 4	550 485	- 4	460 400	- 4
Fabrication Properties		Grade I		Grade II		Grade III
Capacity for being
Cold worked		Poor		Poor		Poor
Hot formed		Fair		Fair		Fair
Machinability Rating		100%		90%		90%
Suitability for soldering		Excellent		Excellent		Excellent
Suitability for Brazing		Good		Good		Good
Uses
Precision Components, Hardware, Hinges, Lock Bodies, Screws, Nuts & Bolts
Gr II : Gear, Pinions, Precision, Automobile, Electronic Parts
Gr III : Precision Components Machining with Riveting Operation

Meeting the demands of our clients, we are engaged in offering quality range of Specialized Brass Wires that are available in varied sizes. Manufactured in compliance with industrial standards these wires have gained wide appreciation for superior strength and durability.

We are one of the leading manufacturer and suppliers of Brass Brazing Wire with the using of a high quality of material, As per the industry standards.

Equivalent Specification

• DIN 8513
• EN 1044
• ISO 17672 ( 2010-11)
• Aws A5.8.89

Product Details:

• Material : Brass Brazing
• Diameter : 2-2.5 mm, 0-0.5 mm, 1.5-2 mm, 0.5-1 mm, >2.5 mm, 1-1.5 mm
• Gauge : 26 SWG, 22 SWG, 18 SWG
• Composition (Tin/Lead) : 60/40, 63/67
• Thikness : 0.1-6

Chemical Requirements	L-CuZn40	Mn2
Copper	60	60
Zinc	39.7	39.7
Silicon	0.3	0.3
Mn	-	0.2
Uses
Use for brass brazing ,steels malleable cast iron, copper,
copper alloy with melting temperatures greater than 950°C (Solidous), nickel, nickel alloys.
Mn2 Use for copper, cast and malleable iron brazing.

Yes! I am Interested

The entire range of Brass Wire for Leaded Ball Pen Tip is manufactured using finest quality of brass procured from reliable and certified sources of the market. These wires are valued for their resistivity against thermal conductivity, longer operational life, low maintenance and strength. We also specialize in field of customization to offer complete client satisfaction. These are manufactured in compliance with industrial standards and finds application in various sectors.

Chemical Requirements
Copper	56.0 - 59.0%
Lead	2.5 to 3.50%
Iron	0.05% max
Zinc	Remainder
Total Imp.	0.35% max
Physical Properties
Size (mm)	T.S.Kg/mm2	EL% Min
1.60 mm R	50 - 60	6 - 10%
1.98 mm R	50 - 60	6 - 10%
2.25 mm R	50 - 60	6 - 10%
2.30 mm R	50 - 60	6 - 10%
2.70 mm R	50 - 60	6 - 10%
Fabrication Properties
Capacity for being
Cold Heading	Fair
Machinability	100%
Plating	Good
Uses
Ball Pens Industries for Writing Pens

Yes! I am Interested

Nickel silver wire is a copper alloy with nickel & sometimes with zinc as well. It is known to have a composition of 60% Copper, 20% nickel and 20% Zinc. We offer a premium quality range of Nickel Silver Wire for Ball Pen Tip, which is acknowledged for its resistance corrosion, high strength and high conductivity. Due to our high-powered conductivity and Eddey current tests, we have been able to fabricate and export defect less range of nickel plated wire.

Specifications:

• Material: Nickel Silver
• Colour: Silver
• Thickness: 0.2.5-7 mm

Ask for Price		Ask for Price
Nickel Silver Wires for Ball Pen Tips Application		Nickel Silver Wire for Various Application

Chemical Requirements
Copper	42.0 - 47.0%
Lead	1.0 to 2.2%
Iron	0.30% max
Nickel	9.0 to 12.0%
Manganese	4.0 to 7.0%
Zinc	Remainder
Total Imp.	0.30% max
Physical Properties
Size (mm)	T.S.Kg/mm2	EL% Min
1.20 mm R	65 - 75	6 - 15%
1.60 mm R	65 - 75	6 - 15%
1.98 mm R	65 - 75	6 - 15%
2.30 mm R	70 - 80	6 - 15%
2.50 mm R	70 - 80	6 - 15%
Fabrication Properties
Capacity for being
Cold Heading	Fair
Machinability	80%
Plating	Not Require
Uses
Ball Pens Industries for Writing Pens

Yes! I am Interested

We provide High Quality Brass flat Wire with Bright surface finishing and brass colour,widely uses in Zipper Industries suitable for teeth formation ,bending and punching work, top and bottam stopper. And suitable for electronic industries for punching work

Equivalent Specification
Germany DIN	Europe EN	Inter.StandardOrg.ISO	USA UNS	Japan JIS	France NS	United Kingdom BS
CuZn37	CuZn37	CuZn37	C27200	C2720	CuZn37	CZ108
CuZn30	CuZn30	CuZn30	C26000	C2600	CuZn30	CZ106

Chemical Composition	CuZn37	CuZn30
Copper	62-64%	68-71%
Lead	40 ppm (max)	40 ppm (max)
Iron	100 ppm (max)	100 ppm (max)
Zinc	Rem	Rem
Impurities	0.2 Max	0.2 Max

Size: Available
	Min	Max	Tolerence
Width:	2.5 mm	10 mm	+/-0.03 mm
Thickness	0.80mm	2.00mm	+/-0.02mm
Hardness	90 HV	170HV
Coil Weight		30-50 Kgs
Coil I.D.		300 mm
Coil Width		100 mm

Yes! I am Interested

Copper alloys are base metal alloys used for high temperature brazing of steels or tungsten carbide. Cost effective alternative to silver brazing alloys wherein high joint strength can be readily achieved. Some alloys also offer excellent corrosin resistance with thermal and electrical conductivity. we offer these alloys in standard composition to suitable specific application available in wires and rods.

GermanyDIN	Europe EN	Inter.StandardOrg.ISO	Aws
Din:8513	En1044	17672(2010-11)	A5.8.89

Chemical Composition	L-CuZn40	Mn2
Copper	60	60
Zinc	39.7	39.7
Silicon	0.3	0.3
Mn	-	0.2
Uses
Use for brass brazing ,steels malleable cast iron, copper,
copper alloy with melting temperatures greater than 950°C (Solidous), nickel, nickel alloys.
Mn2 Use for copper, cast and malleable iron brazing.

Yes! I am Interested

We provide High Quality Brass flat Wire with Bright surface finishing and brass colour,widely uses in Zipper Industries suitable for teeth formation ,bending and punching work, top and bottam stopper.

And suitable for electronic industries for punching work.

Equivalent Specification
Germany DIN	Europe EN	Inter.StandardOrg.ISO	USA UNS	Japan JIS	France NS	United Kingdom BS
CuZn37	CuZn37	CuZn37	C27200	C2720	CuZn37	CZ108
CuZn30	CuZn30	CuZn30	C26000	C2600	CuZn30	CZ106

Chemical Composition	CuZn37	CuZn30
Copper	62-64%	68-71%
Lead	40 ppm (max)	40 ppm (max)
Iron	100 ppm (max)	100 ppm (max)
Zinc	Rem	Rem
Impurities	0.2 Max	0.2 Max

Size: Available
	Min	Max	Tolerence
Width:	2.5 mm	10 mm	+/-0.03 mm
Thickness	0.80mm	2.00mm	+/-0.02mm
Hardness	90 HV	170HV
Coil Weight		30-50 Kgs
Coil I.D.		300 mm
Coil Width		100 mm