Brass Brazing Rod/Wire

Brass Brazing Wire
Brass Brazing Wire
We are one of the leading manufacturer and suppliers of Brass Brazing Wire with the using of a high quality of material, As per the industry standards.

Equivalent Specification
Product Details:
Chemical Requirements L-CuZn40 Mn2
Copper 60 60
Zinc 39.7 39.7
Silicon 0.3 0.3
Mn - 0.2
Uses
Use for brass brazing ,steels malleable cast iron, copper,
copper alloy with melting temperatures greater than 950°C (Solidous), nickel, nickel alloys.
Mn2 Use for copper, cast and malleable iron brazing.


Equivelent Specifications:
ISO 24373:2008 USA JapanEurope Germany
Numerical
symbol
Chemical
symbol
AWS A5.7
/
A5.7M:2007
UNSJIS Z3341
:1999
EN 13347
:2002
EN 14640
:2005
DIN 1733-1
:1998
  AWS A5.8
/
A5.8M:2004
 JIS Z3202
:1999
   
Cu 4641CuZn40SnSi---CuZn40FeSiSnCuZn40SnSi-
Cu 4700CuZn40SnRBCuZn-AC47000GCuZnSnCuZn40Sn1CuZn40-
Cu 6800CuZn40NiRBCuZn-BC68000-CuZn39Fe1
Sn1MnNiSi
CuZn40Ni-
Cu 6810CuZn40Fe1Sn1RBCuZn-CC68100-CuZn40FeSiSnCuZn40SnSi2.0366
Cu 7730CuZn40Ni10Sn1RBCuZn-DC77300GCuZnNi-CuZn40Ni10-



CUZn40SnSi Brass Brazing Rods

CUZn40SnSi Brass Brazing Rods
CUZn40SnSi Brass Brazing Rods
Shree Extrusions is a copper-zinc brazing filler metal similar to RBCuZn-B, but without the addition of nickel. Low Fuming Bronze is a popular brazing alloy for copper, copper alloys, nickel, nickel alloys, steel, and stainless steel. It is also used in thermal spray and arc spray metallizing applications.












Equivelent Specifications:
SPECIFICATIONS DESIGNATION
ISO 24373:2008CUZn40SnSi
DIN-
EN CuZN40FeSiSn

Chemical Composition:
CuAlFeMnPbSiSnZn others
Min(%)58.0 to 62.00.010.20.30.030.10 to 0.501Bal0.2
Max(%)

Physical and Mechanical Properties
Solidus Temperature890°C (1634°F)Liquidus Temperature910°C (1670°F)
Density8.4 gms/cm3Tensile Strength381 N/mm2
Elongation30%Brinell Hardness88HB

Sizes Available
Wire1.0 mm to 11 mm Max


RBCuZn-A Brass Brazing Rods

RBCuZn-A Brass Brazing Rods
RBCuZn-A Brass Brazing Rods
RBCuZn-A Naval Bronze (RBCuZn-A) is a copper-zinc brazing filler metal containing small amounts of tin to improve strength and corrosion resistance in the weld deposit. It is a good choice when the high strength properties of low fuming bronze are not required. A borax-boric acid flux is generally required when brazing with this product.










Equivelent Specifications:
SPECIFICATIONS DESIGNATION
UNSC47000
ISO 24373:2008CuZn40Sn
DIN-
EN 14640:2005CuZN40

Chemical Composition:
CuAlSnZnPbOthers
Min(%)57.0 to 61.00.010.25 to 1.00Bal0.050.5
Max(%)

Physical and Mechanical Properties
Solidus Temperature886°C (1627°F)Liquidus Temperature901°C (1654°F)
Density8.45 gms/cm3Tensile Strength375 N/mm2
Elongation35%Brinell Hardness85HB

Sizes Available
Wire1.0 mm to 11 mm Max


CuZn40Sn1 Brass Brazing Rods

CuZn40Sn1 Brass Brazing Rods
CuZn40Sn1 Brass Brazing Rods
Brazing filler metal is used on steels, copper, copper alloys, nickel, nickel alloys, and stainless steel where corrosion resistance is not of importance. Includes bicycle industry, marine propeller, furniture industry etc.












Equivelent Specifications:
SPECIFICATIONS DESIGNATION
UNSC47000
ISO 24373:2008CuZn40Sn
DIN-
EN 14640:2005CuZN40

Chemical Composition:
CuAlSnZnPbOthers
Min(%)57.0 to 61.00.010.25 to 1.00Bal0.050.5
Max(%)

Physical and Mechanical Properties
Solidus Temperature886°C (1627°F)Liquidus Temperature901°C (1654°F)
Density8.45 gms/cm3Tensile Strength375 N/mm2
Elongation35%Brinell Hardness85HB

Sizes Available
Wire1.0 mm to 11 mm Max


RBCuZn-B Brass Brazing Rods

RBCuZn-B Brass Brazing Rods
RBCuZn-B Brass Brazing Rods
RBCuZn-B Nickel Bronze (RBCuZn-B) brazing filler metal is similar to naval bronze but contains manganese and iron which increase the hardness and strength of the weld deposit. It also contains nickel ensuring uniform distribution of the iron in the deposit. A neutral or slightly oxidizing flame and a boric acid/boric type flux should be used.










Equivelent Specifications:
SPECIFICATIONS DESIGNATION
ASTM/AWS A5.8RBCuZn-B
ISO 24373:2008CuZn40Ni
DIN-
EN 14640:2005CuZn40Ni

Chemical Composition:
CuNiAlFeMnPbSiSnZnothers
Min(%)56.0 to 60.00.20 to 0.800.010.25 to 1.200.01 to 0.500.50.04 to 0.200.80 to 1.10Bal0.5
Max(%)

Physical and Mechanical Properties
Solidus Temperature886°C (1627°F)Liquidus Temperature882°C (1654°F)
Density8.39 gms/cm3Tensile Strength450 N/mm2
Elongation25%Brinell Hardness96HB

Sizes Available
Wire1.0 mm to 11 mm Max


C68000 Brass Brazing Rods

C68000 Brass Brazing Rods
C68000 Brass Brazing Rods
Low-Fuming Bronze-Nickel,This braze welding rod are similar to RBCuZn-A rods but contain additions of iron and manganese which serve to increase the hardness and strength. In addition, a small amount of silicon serves to control the vaporization of the zinc, yielding the “low-fuming” property. The nickel addition assures uniform distribution of the iron in the deposit.










Equivelent Specifications:
SPECIFICATIONS DESIGNATION
UNSC68000
ISO 24373:2008CuZn40Ni
DIN-
EN 14640:2005CuZn40Ni

Chemical Composition:
CuNiAlFeMnPbSiSnZnothers
Min(%)56.0 to 60.00.20 to 0.800.010.25 to 1.200.01 to 0.500.50.04 to 0.200.80 to 1.10Bal0.5
Max(%)

Physical and Mechanical Properties
Solidus Temperature866°C (1591°F)Liquidus Temperature882°C (1620°F)
Density8.39 gms/cm3Tensile Strength450 N/mm2
Elongation25%Brinell Hardness96HB

Sizes Available
Wire1.0 mm to 11 mm Max


RBCuZn-C Brass Brazing Rods

RBCuZn-C Brass Brazing Rods
RBCuZn-C Brass Brazing Rods
Shree Extrusions Low fuming bronze is a general-purpose, copper base alloy brazing rod used extensively for gas brazing steel, copper alloys, cast iron, nickel alloys and stainless steel. Its low fuming characteristic and good mechanical properties make this alloy a widely used general-purpose product. Preheating is recommended for some applications and a bronze brazing flux is required if the rod is not coated. This brazing rod has a low melting point making it easily machinable and excellent for sheet metal work. This alloy also possesses high tensile strength and good ductility.






Equivelent Specifications:
SPECIFICATIONS DESIGNATION
ASTM/AWS A5.8RBCuZn-C
ISO 24373:2008CUZn40Fe1Sn1
DIN2.0366
ENCuZn40FeSnSi

Chemical Composition:
CuAlFeMnPbSiSnZnothers
Min(%)56.0 to 60.00.010.25 to 1.200.01 to 0.500.050.04 to 0.150.80 to 1.10Bal0.5
Max(%)

Physical and Mechanical Properties
Solidus Temperature866°C (1591°F)Liquidus Temperature882°C (1630°F)
Density8.4 gms/cm3Tensile Strength450 N/mm2
Elongation30%Brinell Hardness96HB

Sizes Available
Wire1.0 mm to 11 mm Max


C68100 Brass Brazing Rods

C68100 Brass Brazing Rods
C68100 Brass Brazing Rods
Shree Extrusion Low Fuming Bronze is a general purpose oxy-acetylene brazing rod used for Steel, Copper Alloys, Cast Iron, Nickel Alloys and Stainless Steel.A balanced chemical analysis of Copper and Zinc as well as alloying elements of Tin, Iron, Manganese and Silicon produce welds with excellent mechanical properties.High strength, ductile and sound welds are easily attained by using a neutral or slightly oxidizing flame (especially on Copper Alloys).The high Silicon content keeps fumes to a minimum.






Equivelent Specifications:
SPECIFICATIONS DESIGNATION
UNSC68100
ISO 24373:2008CUZn40Fe1Sn1
DIN2.0366
ENCuZn40FeSnSi

Chemical Composition:
CuAlFeMnPbSiSnZnothers
Min(%)56.0 to 60.00.010.25 to 1.200.01 to 0.500.050.04 to 0.150.80 to 1.10Bal0.5
Max(%)

Physical and Mechanical Properties
Solidus Temperature866°C (1591°F)Liquidus Temperature888°C (1630°F)
Density8.4 gms/cm3Tensile Strength450 N/mm2
Elongation30%Brinell Hardness96HB

Sizes Available
Wire1.0 mm to 11 mm Max


RBCuZn-D Brass Brazing Rods

RBCuZn-D Brass Brazing Rods
RBCuZn-D Brass Brazing Rods
RBCuZn-D Nickel Silver (RBCuZn-D) is a bare brazing rod used widely as a replacement for high cost silver brazing alloys when higher brazing temperatures are acceptable. The weld deposits have a very high tensile strength, good ductility and excellent corrosion resistance. Nickel Silver weld deposits are also readily machinable and will not work harden when put into service. A neutral or slightly oxidizing flame is recommended.






Equivelent Specifications:
SPECIFICATIONS DESIGNATION
ASTM/AWS A5.8 RBCuZn-D
ISO 24373:2008CuZn40Ni10Sn1
JISGCuZnNi
ENCuZN40Ni10

Chemical Composition:
CuAlFeMnPbSiSnZnothers
Min(%)46.0 to 50.00.01--0.050.04 to 0.25-Bal0.5
Max(%)

Physical and Mechanical Properties
Solidus Temperature890°C (1634°F)Liquidus Temperature935°C (1630°F)
Density8.40 gms/cm3Tensile Strength385 N/mm2
Elongation25%Brinell Hardness120HB

Sizes Available
Wire1.0 mm to 11 mm Max




Product Range

Brass Wires Specialized Brass Wires Brass Rods Specialized Copper Alloy Rods Ingots & Billet
Copper & Copper Alloy Tubes Bronze Rods Brass Tubes Copper Nickel
BRASS ALLOYS
Leaded Brass Naval Brass Nickel Silver Brass Red Brass Yellow Brass
Other Brass
BRONZE ALLOYS
Aluminum Bronze Silicon Aluminum Bronze High Tensile Manganese Bronze Nickel Aluminum Bronze
COPPER ALLOYS
C11000 Electrolytic Tough Pitch Copper Nickel Leaded Copper Other Copper

Home About Us Product Range Quality We Provide Industrial Applications Certifications Company Video Enquiry

Member IndiaMART© Shree Extrusions Limited. All Rights Reserved (Terms of Use)
Developed and Managed by IndiaMART InterMESH Limited